Addicon F
Addicon F
Addicon F is a highly concentrated, premium grade structural polymer latex emulsion specifically engineered as a water-resistant admixture and high performance modifier for cement mortars and concrete applications.
Technical Property | Value / Description | Engineering Benefit |
Classification | High-Performance Waterproofing Polymer Latex Admixture | Multi-action mechanical modifier for impermeable and resilient mortars |
Chemical Base | Advanced Concentrated Pure Polymer Latex Liquid Matrix | Formulates a highly compact, non-porous polymer-cement composite frame |
Water Impermeability | Exceptional Rating (Capillary Pore-Sealing Effect) | Provides robust defense against hydraulic pressure and moisture tracking |
Bonding Strength | Outstanding Interfacial Adhesion Performance | Eradicates structural failure or peeling of repair mortars and renders |
Shrinkage Control | Complete Protection against structural drying cracks | Absorbs internal setting strains, stabilizing massive facade plaster planes |
Addicon-F
Absolute Water & Hydrostatic Pressure Defense: Transforms conventional mineral mortars into fully cohesive, watertight, and vapor-shielded layers.
Ironclad Polymer Interface Anchoring: Provides permanent physical and chemical adhesion parameters for structural overlays without failing.
Anti-Shrinkage & Crack Elimination: Mitigates internal dry setting movements, entirely dropping surface hairline cracks or checking phenomena.
Enhanced Mechanical Toughness: Radically updates the cured plaster matrix tensile strength, flexing properties, and abrasion resistance.
Chemical & Chloride Barrier Protection: Safeguards underlying structures from the tracking of aggressive salt efflorescence, environmental carbonation, and sulfates.
Essential waterproof additive for rendering, spatter-dash (Tartasha), and general masonry plasters in bathrooms, kitchens, and storm-exposed external facades.
Formulating continuous technical bonding slurries to securely connect fresh concrete toppings to aged structural concrete platforms.
Upgrading and fortifying cementitious tile adhesives, porcelain mortars, and performance grouts inside swimming pools and industrial wet zones.
Preparing non-shrink high-bond repair mortars to manage concrete structural honeycombing and spalls in water storage tanks and water-retaining structures.
Substrate Profiling: Target surfaces must be completely structural sound, clear of fine dust, formwork release oils, micro-fragments, or loose coats. Fully pre-saturate the dry porous masonry background with fresh clean water prior to execution, ensuring no standing ponding water is left.
Slurry Bonding Protocol (Wet-on-Wet): Mix Addicon F with clean potable water at a 1:1 volumetric ratio, then add fresh cement gradually under mixing until a smooth bonding slurry is achieved. Apply by brush onto the prepared face and lay the fresh mortar or concrete immediately while the slurry base is wet.
Mortar Modification Mix: Integrate Addicon F directly into the batch gauging water at a dosage range of 10% to 20% by weight of cement, matching specialized technical project configurations, then conduct structural mixing sequences as standard.
Site Restrictions & Curing: Do not apply if ambient layout temperature falls below 5°C. Properly cure the modified cement mortar layout with light clean water misting post-initial setting to reach targeted hydraulic cement properties.